<p> A process of hardening the face of steel, as armor plates, invented by Hayward A. Harvey of New Jersey, consisting in the additional carburizing of the face of a piece of low carbon steel by subjecting it to the action of carbon under long-continued pressure at a very high heat, and then to a violent chilling, as by a spray of cold water. This process gives an armor plate a thick surface of extreme hardness supported by material gradually decreasing in hardness to the unaltered soft steel at the back. </p> | Harvey Process <ref name="term_125608" /> | ||
==References == | <p> [[A]] process of hardening the face of steel, as armor plates, invented by Hayward [[A.]] Harvey of New Jersey, consisting in the additional carburizing of the face of a piece of low carbon steel by subjecting it to the action of carbon under long-continued pressure at a very high heat, and then to a violent chilling, as by a spray of cold water. This process gives an armor plate a thick surface of extreme hardness supported by material gradually decreasing in hardness to the unaltered soft steel at the back. </p> | ||
== References == | |||
<references> | <references> | ||
<ref name="term_125608"> [https://bibleportal.com/dictionary/webster-s-dictionary/harvey+process Harvey Process from Webster's Dictionary]</ref> | <ref name="term_125608"> [https://bibleportal.com/dictionary/webster-s-dictionary/harvey+process Harvey Process from Webster's Dictionary]</ref> | ||
</references> | </references> |
Latest revision as of 04:47, 13 October 2021
Harvey Process [1]
A process of hardening the face of steel, as armor plates, invented by Hayward A. Harvey of New Jersey, consisting in the additional carburizing of the face of a piece of low carbon steel by subjecting it to the action of carbon under long-continued pressure at a very high heat, and then to a violent chilling, as by a spray of cold water. This process gives an armor plate a thick surface of extreme hardness supported by material gradually decreasing in hardness to the unaltered soft steel at the back.